Title: Caracterização físico-mecânica e biológica de cimentos experimentais à base de MTA para o complexo dentino-pulpar
Other Titles: Physico-mechanical and biological experimental-based MTA for pulp-dentin complex cements
metadata.dc.creator: Dantas, Raquel Venâncio Fernandes
metadata.dc.contributor.advisor1: Demarco, Flávio Fernando
metadata.dc.contributor.advisor-co1: Zanchi, Cesar Henrique
metadata.dc.description.resumo: Há necessidade de desenvolvimento de novos cimentos odontológicos para otimizar as estratégias da terapia pulpar. Este estudo objetivou avaliar características físico-mecânica e biológica de cimentos experimentais (Híbrido, Pasta e Resinoso), comparando-os ao MTA (Angelus®, Londrina, PR, Brasil) e um cimento de ionômero de vidro, desenvolvido em nosso laboratório. Para os testes físico-mecânico e biológico, espécimes com dimensões padrão foram confeccionados. Para o pH, os espécimes foram imersos em meio de cultura (DMEM) enriquecido com SFB (soro fetal bovino) e analisados por pH-metro digital nos tempos: 3, 24, 48 e 72h. Para a resistência à tração diametral, espécimes cilíndricos foram submetidos a carga compressiva até a fratura. Na avaliação da citotoxidade, células 3T3 foram cultivadas e expostas aos eludatos dos cimentos. A viabilidade celular foi determinada utilizando o teste MTT. Os resultados foram analisados utilizando análise de variância (ANOVA) e teste de Tukey (p<0,05). O grupo Pasta apresentou valores de pH semelhantes ao MTA, assim como o grupo Híbrido seguiu os parâmetros do CIV (p>0,05).Todos os materiais apresentaram valores de pH alcalinos ou próximos a neutralidade nos tempos avaliados. O MTA e o CIV apresentaram resultados de resistência similares. Os menores e maiores valores observados foram do grupo Pasta e Resinoso, respectivamente (p<0,05). A viabilidade celular para os grupos MTA, Híbrido, Pasta, Resinoso, quando comparados ao grupo controle foi de: 49, 93, 90 e 86%, respectivamente. Considerando este estudo in vitro, nós concluímos que o cimento experimental Resinoso, que é fotoativado, apresentou desempenho similar ou superior aos materiais controles testados
Abstract: There is a need to develop new cements to optimize pulp therapy strategies. The aim of this study was evaluate physic-chemical and biological parameters of experimental cements (Hybrid, Paste and Resinous), including pH, diametral tensile strength and cytotoxicity of these experimental cements comparing them to MTA (Angelus®, Londrina, PR, Brazil) and a glass ionomer cement developed in our laboratory. For the physic-mechanical and biological tests specimens with standard dimensions were produced. For pH measurement, specimens were immersed in culture medium (DMEM) supplemented with FBS (fetal bovine serum) and analyzed by digital pH meter at 3, 24, 48 and 72h. For diametral tensile strength test the specimens were subjected to compressive load until the fracture. To evaluate cytotoxicity 3T3 cells were cultured and exposed to the cement eluates. The cell viability was detected using MTT test. The results were analyzed using analysis of variance (ANOVA) and Tukey's test (p <0.05). The Paste group showed pH values similar to the MTA, as well as the Hybrid group was similar to the GIC group (p> 0.05). All materials presented alkaline pH values or were near to neutrality on evaluated times. MTA and GIC showed similar strength results. The lowest and highest strength values were observed in groups Paste and Resinous, respectively (p <0.05). Cell viability for MTA, Hybrid, Paste and Resinous groups, were 49, 93, 90 and 86% respectively, when compared to the control group. Considering this in vitro study, we concluded that the photo-cured Resinous experimental cement presented a performance similar or superior to the commercial or other experimental materials tested
Keywords: Polpa dentária
Cimentos odontológicos
Biocompatibilidade
Propriedades mecânicas
Dental pulp
Dental cements
Biocompatibility
Mechanical Properties
metadata.dc.subject.cnpq: CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA
metadata.dc.language: por
metadata.dc.publisher.country: BR
Publisher: Universidade Federal de Pelotas
metadata.dc.publisher.initials: UFPel
metadata.dc.publisher.department: Odontologia
metadata.dc.publisher.program: Programa de Pós-Graduação em Odontologia
Citation: DANTAS, Raquel Venâncio Fernandes. Physico-mechanical and biological experimental-based MTA for pulp-dentin complex cements. 2011. 69 f. Dissertação (Mestrado em Odontologia) - Universidade Federal de Pelotas, Pelotas, 2011.
metadata.dc.rights: OpenAccess
URI: http://hdl.handle.net/123456789/2283
Issue Date: 28-Oct-2011
Appears in Collections:PPGO: Dissertações e Teses

Files in This Item:
File Description SizeFormat 
Dissertacao_Raquel_Venancio_Fernandes_Dantas.pdf1,53 MBAdobe PDFThumbnail
View/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.