Title: Análise do desempenho de condicionadores experimentais no tratamento de ligas metálicas
Other Titles: Evaluation of experimental conditioners in the metal alloys treatment
metadata.dc.creator: Azevedo, Eduardo Costa de
metadata.dc.contributor.advisor1: Camacho, Guilherme Brião
metadata.dc.contributor.advisor-co1: Pinto, Márcia Bueno
metadata.dc.description.resumo: O objetivo deste estudo foi avaliar o desempenho de três condicionadores experimentais em ligas metálicas de diferentes composições químicas, através de testes de microcisalhamento e análise de fratura. Três ligas metálicas (NiCr, AgPd, AgAu) foram fundidas em forma de disco (3x10 mm) e suas superfícies foram preparadas com lixas d água (400, 600 e 1200#). Todos os grupos receberam um tratamento superficial com quatro condicionadores, sendo três experimentais e um comercial (Alloy Primer- Kuraray Medical Corporation, Kurashiki, Okayama, Japão) que serviu de controle. Logo após o condicionamento, foi aplicado o adesivo do sistema Adper Scotchbond (3M Dental Products Division, Saint Paul, MN, EUA) e sobre este foram confeccionados os corpos de prova com um cimento resinoso de ativação dupla Rely X ARC (3M Dental Products Division, Saint Paul, MN, EUA) com uma área de adesão de 1,13 mm2. O adesivo e o cimento resinoso utilizados foram fotoativados com aparelho LED SDI Radii® (1400mW/cm2) por 40 segundos. Os ensaios mecânicos foram executados com velocidade de 0,5 milímetros por minuto. Os valores de resistência adesiva foram registrados em MPa (N/mm2 = Newton/milímetro2) e submetidos a Análise de Variância e teste complementar de Tukey para detectar diferença entre as médias (p < 0,05). A análise da superfície de fratura foi observada através de microscopia óptica com um aumento de 40X sendo classificada como falha adesiva, mista ou coesiva. Os condicionadores experimentais não apresentaram um fator de desempenho satisfatório devido à variação das médias nos substratos metálicos utilizados. Houve predominância de falha do tipo adesiva. Baseado na metodologia foi possível concluir que os condicionadores experimentais apresentaram resistência de união significante nos grupos avaliados, porém necessitam de modificações para alcançarem valores mais aproximados ao material comercial
Abstract: The aim of this study was to investigate the performance of three experimental surface conditioners on metal alloys of different chemical composition, through microshear tests and failure analysis. Three metal alloys (NiCr, AgPd, AgAu) were melted in disc-shaped specimens (3mm in thickness x 10mm in diameter) and their surfaces were polished with aluminum oxide abrasive papers (400-, 600- and 1200-grit). The groups were treated with one of the experimental surface conditioners, and a commercial material (Alloy Primer Kuraray) was used as a control. The bonding agent of the Adper Scotchbond system (3M) was applied, and cylindrical specimens were made with a resin cement (Rely X ARC 3M), with an adhesion area of 1.13mm2. The bonding agent and the cement were light-activated for 40s (LED SDI Radii® - 1400mW/cm2). The micro-shear test was conducted at a cross-head speed of 0.5mm/min. Bond strength values were calculated in MPa (N/mm2) and submitted to ANOVA and Tukey s post-hoc test (p<0.05). Fractographic analyzes were performed under optical microscopy (40X) and classified as adhesive, mixed or cohesive. The experimental surface conditioners did not present a satisfactory performance factor due to the means variation in the metal alloys used in the study. A predominance of adhesive failures was detected. In conclusion, the experimental surface conditioners presented a significant adhesion to all metal alloys. However, these materials need modifications to obtain values more approximate to the commercial material
Keywords: Primer para metal
Microcisalhamento
Resistência de união
Ligas metálicas
Metal primer
Micro-shear
Bond strength
Dental materials
Metal alloys
Materiais dentários
metadata.dc.subject.cnpq: CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA
metadata.dc.language: por
metadata.dc.publisher.country: BR
Publisher: Universidade Federal de Pelotas
metadata.dc.publisher.initials: UFPel
metadata.dc.publisher.department: Odontologia
metadata.dc.publisher.program: Programa de Pós-Graduação em Odontologia
Citation: AZEVEDO, Eduardo Costa de. Evaluation of experimental conditioners in the metal alloys treatment. 2007. 49 f. Dissertação (Mestrado em Odontologia) - Universidade Federal de Pelotas, Pelotas, 2007.
metadata.dc.rights: OpenAccess
URI: http://hdl.handle.net/123456789/2296
Issue Date: 19-Dec-2007
Appears in Collections:PPGO: Dissertações e Teses

Files in This Item:
File Description SizeFormat 
Dissertacao_Eduardo_Costa_de_Azevedo.pdf689,49 kBAdobe PDFThumbnail
View/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.